The service life of acid resistant brick generally depends on the quality of acid resistant brick itself, and then the quality of auxiliary materials and the operation of construction process. When purchasing acid resistant brick, we must strictly follow the selection method of acid resistant tile as the material selection standard. The material selection is appropriate and the quality of auxiliary materials is qualified. The rest is the construction problem. The specific construction method of acid resistant brick As mentioned earlier, the minor editor here mainly talks about the hazards of improper construction.
1. The auxiliary materials are not solid, and there are bubbles or voids in the middle. It is easy to cause the leakage of liquid in the reaction tank and cause the brick to fall off.
2. The acid resistant brick breaks. When cutting the tile during the construction, or accidentally cracks the tile, making the liquid enter the plain surface of the acid resistant brick. Cause corrosion.
3. The matrix is not smooth, resulting in the gap between the acid resistant brick and the matrix. In the later use, due to physical collision or noon pressure, it will break and damage in use.
4. The surface of the base or acid resistant brick is not clean, and the acid resistant brick is not fully fixed with the base during construction. Cause construction failure. Affect service life.